Friction stir welded joints in aluminum highway bridge decks: a quality control framework
article
Friction stir welding (FSW) has shown considerable promise for highway aluminum bridge deck fabri cation but lacks specific quality control guidelines for fit-up defects. This study conducts a perform ance-based (PB) quality control assessment of butt-lap FSW joints for highway bridge decks. Five FSW conditions were simulated, including a standard control welding condition, fit-up defects (gaps and tool offset), and a welding tool’s rotational direction inversion from the standard condition. A rigorous prequalification process established acceptable tolerance levels for fit-up defects: a 3 mm positive off set, a 1.5 mm negative offset, and a 1.5 mm gap. Subsequently, specimens from real aluminium deck extrusions, incorporating the various welding conditions were subjected to fatigue testing. Results showed that the fatigue strength and failure mode were primarily influenced by the weld root micro structure. The FSW tool’s rotational direction significantly influenced fatigue strength due to its impact on the nucleation of the hooking defect in the weld root area, while the impact of fit-up defects on fatigue strength was comparatively lesser. Furthermore, finite element analysis examined the impact of the geometrical features of the root microstructure and the direction of the initial crack propagation on the stress intensity factor range. These findings have practical implications for setting tolerance lev els for fit-up defects in aluminum butt-lap FSW joints and optimizing of the quality and fatigue strength of butt-lap FSW joints.
Topics
TNO Identifier
1002597
Repository link
Source
Structure and Infrastructure Engineering, pp. 1-21.
Pages
1-21
Files
To receive the publication files, please send an e-mail request to TNO Repository.