Damp heat related degradation mechanisms within CIGS solar cells
conference paper
Degradation rates and mechanisms for molybdenum back contacts and ZnO:Al front contacts exposed to damp heat were obtained from literature and experiments. It was found that molybdenum back contacts with a higher density and covered by a MoSe2 film are more stable than their low density, bare counterparts. For ZnO:Al front contacts various material changes, including thickness, deposition temperatures and doping concentration increase as well as post-deposition treatments can lead to a more stable material. Moreover, the degradation rate of encapsulated and non-encapsulated CIGS solar cells and modules exposed to damp heat were determined It was observed that in general, exposure to damp heat led to a reduction in efficiency, mostly caused by a reduction in Voc and FF. However, it was found that very large differences exist between samples. © 2017 IEEE.
Topics
CIGSDamp heatHumidityModulesSolar cellsStabilityAluminumAtmospheric humidityConvergence of numerical methodsDegradationDepositionII-VI semiconductorsMolybdenumMolybdenum compoundsSelenium compoundsSemiconductor dopingZinc oxideCIGS solar cellsDegradation mechanismDeposition temperaturesDoping concentrationModulesPost deposition treatment
TNO Identifier
810211
ISBN
9781509056057
Publisher
Institute of Electrical and Electronics Engineers Inc.
Source title
44th IEEE Photovoltaic Specialist Conference, PVSC 2017. 25 June 2017 through 30 June 2017
Pages
1-6
Files
To receive the publication files, please send an e-mail request to TNO Repository.