Leading edge erosion of coated wind turbine blades: review of coating life models
article
Erosion of the leading edge of wind turbine blades by droplet impingement wear, reduces blade aerodynamic efficiency and power output. Eventually, it compromises the integrity of blade surfaces. Elastomeric coatings are currently used for erosion resistance, yet the life of such coatings cannot be predicted accurately. This review paper gives an overview of experimentally validated erosion model blocks that can be used to predict the life of the leading edge of coated wind turbine blades. From the reviewed work it is concluded that surface fatigue, as nucleating wear mechanism for erosion damage, can explain erosive wear and failure of the coatings. An engineering approach to surface fatigue, using the PalmgreneMiner rule for cumulative damage, allows for the construction of a rain erosion incubation period equation. Coating life was described as a function of the rain intensity, the droplet diameter, the fatigue properties of the coating and the severity of the conditions. It is recommended to focus coating development on reduction of the impact pressure, e.g. by developing surfaces with a low modulus of elasticity; or on enlarging the safe area by: developing coatings with adjustable compressive stresses and hardness, or coatings without defects and impurities.
TNO Identifier
525117
ISSN
0960-1481
Source
Renewable Energy, 80, pp. 837-848.
Publisher
TNO
Collation
12 p.
Place of publication
Eindhoven
Pages
837-848
Files
To receive the publication files, please send an e-mail request to TNO Repository.