Title
Bias-Dependent Stability of Perovskite Solar Cells Studied Using Natural and Concentrated Sunlight
Author
Anoop, K.M.
Khenkin, M.V.
Di Giacomo, F.
Galagan, Y.
Rahmany, S.
Etgar, L.
Katz, E.A.
Visoly-Fisher, I.
Publication year
2019
Abstract
Degradation rates in perovskite solar cells (PSCs) were previously shown to be bias dependent; however, little is known about the mechanisms and driving factors that account for such degradation. Herein, stability studies under concentrated sunlight are demonstrated as a powerful experimental methodology to investigate bias-dependent PSC degradation mechanisms. Stress testing of encapsulated PSCs’ stability shows that light intensity is more significant than the illumination dose for PSC degradation under short-circuit (SC) conditions, whereas the dose is the determining factor under open-circuit (OC) stressing. This indicates that different degradation mechanisms are dominant under different bias conditions. It is postulated that degradation at SC biasing is dominated by ion migration, facilitated by photogenerated defects. Degradation at OC biasing can be explained by photogenerated radicals acting as nonradiative recombination centers (charge traps), which are created via reactions with accumulated charge carriers. Trap formation upon OC biasing is in accordance with degradation of photoluminescence and OC voltage (VOC) observed under this stress. A combination of multiple mechanisms, all with reduced driving forces compared with OC /SC biasing, explains degradation at maximum power point biasing. Understanding the bias effect on PSC stability can elucidate the underlying degradation mechanisms and lead to routes to reduce them.
Subject
Industrial Innovation
Bias-dependent degradation rates
Perovskite solar cells
Positive ions
Halide perovskites
Optical absorption properties
Absorption spectroscopy
To reference this document use:
http://resolver.tudelft.nl/uuid:b48e684b-bf95-40a7-ba8a-0beec3056ef8
DOI
https://doi.org/10.1002/solr.201900335
TNO identifier
870183
Publisher
Wiley-VCH Verlag
Source
RRL Solar
Document type
article