Title
Effects of polypropylene fibres in concrete: Microstructure after fire testing and chloride migration
Author
TNO Bouw en Ondergrond
Polder, R.B.
Larbi, J.A.
Publication year
2007
Abstract
Explosive spalling of pieces of concrete from the heated surface is considered to be the most dangerous effect of damage of concrete subjected to intense fire attack, especially when it occurs in restricted areas such as underground tunnels. Recent investigations have revealed that the amount of explosive spalling and the extent of cracking can considerably be reduced by use of suitable amount of polypropylene fibres. However, little attention has been given to exactly how the fibres behave in the matrix of the concrete when exposed to fire. A good insight into the behaviour of the fibres when applied in concrete, especially when subjected to fire, can help optimise their use to reduce explosive spalling. This paper deals with a case study, in which an integrated microscopic method consisting of stereomicroscopy and polarising and fluorescent microscopy were used to assess the effectiveness of the pp-fibres in reducing explosive spalling in concrete elements subjected to fire attack. Rapid Chloride Migration test was also performed on standard specimens to establish whether the presence of the fibres might adversely affect the permeability and durability of the elements.
Subject
Spalling
Polypropylene fibres
Microscopy
Microstructure
Durability
Buildings and Infrastructure
Built Environment
To reference this document use:
http://resolver.tudelft.nl/uuid:33653892-f9f9-4ab9-92d2-4286713a79e0
TNO identifier
331473
Source
Heron, 52 (52), 289-306
Document type
article